[Range of application]

HAF-11 is made by a special non-ionic surfactant compound, suitable for polyester FDY high speed spinning process, spinning speed is up to:. 3000m / min.

[Quality index]

Appearance: light yellow transparent liquid

pH value (1% aq solution.): 6.0-8.0

Kinematic viscosity (40°C, mm 2 / s): 80-100

Active matter: 80 ± 2%

Emulsion stability (10%): colorless transparent liquid, 72h No delamination.

[ Performance and characteristics]

1, oil uniform and stable, high film strength, good permeability.

2, have good high temperature performance, no coking phenomenon applications, which do not have specialized cleaning wire wheels, drawing rollers, etc., to avoid coking and cause breakage, hair times.

3, good thermal stability, low Volatile loss, not because of the volatile oil caused by high production costs, do not pollute the environment, and do not harm the health workers in the operation.

4, HAF-11 spinning oil was about 1%.

5, has excellent antistatic properties, and Antistatic agent can coexist with the most common slurry.

6, oil emulsions have good wetting of the tow, so that high-speed operation can tow rapid adsorption of oil, and quickly auxiliary exhibition on the fiber surface, to achieve uniform oil.

7, the oil can give a better friction performance fibers, the fibers have good bundling properties, bobbin forming good, beneficial shaped wire processing.

8, HAF-11 oil is environmentally friendly, biodegradable monomer is all substance, no mineral oil components, fiber spinning and after processing does not cause any harm to the environment.

[Method of application]

A certain amount of soft water into the reactor deployment, stirring without the addition of preservatives 300-500ppm Stir 5 minutes to measure a good oil to trickle slowly into the reactor deployment, while adding while stirring, plus complete continue stirred for 45 minutes, using a concentration of 10-15%.

[ Packing, storage and transportation ]

50kg plastic drum or 200kg plastic drum.